橡胶同步带
- 产品规则
- 产品特点
T型齿同步带：
| 型号 | 节距 (mm) | 齿高 (mm) | 带厚 (mm) | 角度 β° |
|
| MXL | 2.032 | 0.51 | 1.14 | 40 |
|
| XXL | 3.175 | 0.76 | 1.52 | 50 |
|
| XL | 5.080 | 1.27 | 2.30 | 50 |
|
| L | 9.525 | 1.91 | 3.60 | 40 |
|
| H | 12.70 | 2.29 | 4.30 | 40 |
|
| XH | 22.225 | 6.35 | 11.20 | 40 |
|
| XXH | 31.750 | 9.53 | 15.70 | 40 |
|
| T2.5 | 2.5 | 0.7 | 1.30 | 40 |
|
| T5 | 5 | 1.20 | 2.20 | 40 |
|
| T10 | 10 | 2.50 | 4.50 | 40 |
|
| T20 | 20 | 5.00 | 8.00 | 40 |
|
| AT5 | 5 | 1.20 | 2.70 | 50 |
|
| AT10 | 10 | 2.50 | 5.00 | 50 |
|
| AT20 | 20 | 5.00 | 8.00 | 50 |
|
圆弧齿同步带：
|
齿型代号 |
型号 | 节距 (mm) | 齿高 (mm) | 带厚 (mm) |
|
|
HTD |
2M | 2 | 0.75 | 1.36 |
|
| 3M | 3 | 1.17 | 2.4 |
|
|
| 5M | 5 | 2.06 | 3.8 |
|
|
| 8M | 8 | 3.36 | 6.00 |
|
|
| 14M | 14 | 6.02 | 10.00 |
|
|
| 20M | 20 | 8.4 | 13.20 |
|
|
|
STPD/STS |
S2M | 2 | 0.76 | 1.36 |
|
| S3M | 3 | 1.14 | 2.20 |
|
|
| S4.5M | 4.5 | 1.71 | 2.81 |
|
|
| S5M | 5 | 1.91 | 3.4 |
|
|
| S8M | 8 | 3.05 | 5.3 |
|
|
| S14M | 14 | 5.3 | 10.2 |
|
|
|
RPP/HPPD |
2M | 2 | 0.76 | 1.36 |
|
| 3M | 3 | 1.15 | 1.9 |
|
|
| 5M | 5 | 1.95 | 3.5 |
|
|
| 8M | 8 | 3.2 | 5.5 |
|
|
| 14M | 14 | 6.00 | 10 |
|
橡胶同步带/氯丁胶同步带
(1) 玻璃纤维抗拉层
玻璃纤维抗拉层是由多股玻璃纤维组成的绳索, 沿胶带宽度螺旋形地绕布在胶带的节线位置，其强度高、伸长小、耐腐识蚀和耐热性能良好。(2) 氯丁胶带背
氯丁胶带背它将玻璃纤维牢固地粘合在节线位, 起着保护抗拉材料的作用，在传动中需要使用带背的场合，可防止由于磨擦而引起的损坏，它比聚氨酯同步带背更具有优越的耐水解性和耐热性。
(3) 氯丁胶带齿
带齿由剪切强度高、硬度适当的氯丁胶组成，需要精密的成型和精确的分布位置才能与带轮的齿槽正确啮合，其齿根要与节线保持规定的距离，弯曲时节距无变化。
(4) 尼龙包布层
尼龙包布层是保护胶带的抗磨擦部分，应具优越的耐磨性，是用摩擦系数小的尼龙布组成。
氯丁橡胶同步带的耐水解、耐热、耐冲击性能优于聚氨酯同步带，它的传动功率范围大，特别在大功率传动中，聚氨酯同步带是无法与之相比的。工作温度一般为-34～80 C
聚氨酯同步带：
聚氨脂同步带一般以尼龙线(或钢丝、铜丝)作为抗拉体，聚酯浇注而成，具有耐油、耐冲击、美观等特点。
聚氨脂同步带硬耐磨但导开行不如橡胶同步带.
化学性能
- 防老化、防水解、防紫外线UVA、防臭氧
- 工作温度：-30℃～+80℃短时间可承受最高+110℃
- 高度防油、防油酯
- 抗大多数酸、碱腐蚀
橡胶同步带屈挠性好.耐水性好.PU不耐水.往复工作性差.高低温性能差.耐磨好.在常温静态条件下PU聚氨酯同步带好.反之橡胶同步带好。聚氨酯TPU同步带是一种热塑聚氨酯材料,它具有高模量,高强度,高弹性,永久性变形小,曲绕性好,优良的耐磨,耐油,耐低温,耐老化性能,能达到医疗卫生要求.聚氨酯TPU同步带的耐磨性是橡胶同步带的8倍,比橡胶同步带卫生,更适合用于食品,医疗行业,洁净生产行业.目前TPU同步带已逐渐代替橡胶同步带.TPU同步带广泛应用在电脑绣花机,饮料机械,以及彩色玻璃制造等行业.本公司采用的骨架材料是芳纶线绳,